Deposition of advanced phosphor coatings by flame spray pyrolysis
University thesis:
Hamburg-Harburg, Univ., Institut für Optische und Elektronische Materialien, Diss., 2011
Footnote:
Parallel als Druckausg. im Verl Cuvillier, Göttingen erschienen
Systemvoraussetzungen: Internet-Zugriff, Adobe Acrobat Reader
Description:
Flame aerosol deposition (FAD) combines synthesis of phosphor particles by flame spray pyrolysis and their deposition onto a substrate in a single process step. Y2O3:Eu phosphor coatings consisting of sub-micrometer particles could be deposited by FAD based on droplet-to-particle conversion within minutes and had brightness equal to that of a conventional micrometer-sized phosphor. Screens of Y2O3:Eu nanophosphor produced by chemical vapor condensation FAD had lower brightness but they potentially could facilitate the highest possible (diffraction-limited) optical screen resolution.
Flammenaerosolabscheidung kombiniert in einem Prozessschritt die Synthese von Leuchtstoffpartikeln mittels Flammensprühpyrolyse und deren Abscheidung auf ein Substrat. Schichten von Submikrometer-großen Y2O3:Eu Partikeln, die wir in wenigen Minuten abgeschieden haben, erreichten eine vergleichbare Helligkeit mit Bildschirmen, die mit einem kommerziellen Leuchtstoff hergestellt wurden. Y2O3:Eu Nanoleuchtstoffbe-schichtungen hatten eine niedrigere Helligkeit, bieten aber die Möglichkeit, die höchstmögliche (beugungsbegrenzte) optische Auflösung zu erzielen.