Description:
<jats:p>The magnetization reversal mechanism of a sintered Nd-Fe-B magnet with Dy segregation near grain boundaries (GB) was studied using spin polarized scanning electron spectroscopy and magnetization measurements. More fine magnetic domains near GB were found in the magnet with Dy segregation than in the magnet without treatment. Magnetic modifications near the GB had no effect on the magnetization development. The domain wall motion of a quasihard magnetic component in the magnet with Dy segregation was suppressed in comparison with those in the magnet without treatment; this could also be confirmed in the different behaviors of asymmetry components toward a magnetic field direction between both magnets. From analyzing the probability of rotating magnetization near the GB, the magnetization reversal of the magnet with Dy segregation was more difficult to produce than those of the magnet without treatment.</jats:p>