Media type: E-Article Title: Preparation and evaluation of nanocomposites of polyfuran with Al2O3 and montmorillonite clay Contributor: Ballav, Nirmalya; Biswas, Mukul Published: Wiley, 2004 Published in: Polymer International, 53 (2004) 10, Seite 1467-1472 Language: English DOI: 10.1002/pi.1562 ISSN: 0959-8103; 1097-0126 Keywords: Polymers and Plastics ; Materials Chemistry ; Organic Chemistry Origination: Footnote: Description: AbstractHigh yield oxidative polymerization of furan was accomplished in CHCl3 solvent at 0 °C. A nanocomposite of polyfuran (PF)–Al2O3 was prepared through polymerization of furan in a suspension of nanodimensional Al2O3 in CHCl3 at 0 °C. High yield polymerization of furan was also achieved in montmorillonite clay (MMT) without any extraneous oxidant. The formation of PF was confirmed by FTIR and elemental analysis. Thermogravimetric analyses revealed the following trends in thermal stability: PF < PF–Al2O3 < Al2O3 and PF < PF–MMT < MMT. Scanning electron microscopy showed the average particles sizes to be ca 51 nm and ca 40 nm for PF–Al2O3 and PF–MMT composites, respectively. The occurrence of a peak at 19.84 Å in the X‐ray diffraction pattern of the PF–MMT composite was indicative of the intercalation of PF in MMT lamellae. Transmission electron microscopic analyses for the PF–MMT composite also showed incorporation of PF moieties in‐between the MMT layers. The dc conductivity values (S cm−1) of PF–FeCl3, PF–Al2O3–FeCl3, PF–MMT and PF–MMT–FeCl3 systems were in the order of 10−6, 10−7, 10−8 and 10−7, respectively, and the values were significantly enhanced compared to the dc conductivity value of PF homopolymers (10−11). Copyright © 2004 Society of Chemical Industry