Description:
<jats:p>In contrast to high silica zeolites, it is difficult to obtain mesoporosity in zeolites with low Si/Al ratio (e.g., <20) via conventional NaOH-based treatment, making the obtainment of hierarchical zeolites with high acidity a challenging target. In this paper, we report the preparation of hierarchical FER-type zeolite at low Si/Al molar ratio (about 10) by postsynthesis etching involving a sequence of three treatments with NaAlO<jats:sub>2</jats:sub>, HCl, and NaOH solutions and investigate the effect of both NaAlO<jats:sub>2</jats:sub> solution concentration and time of treatment on the textural properties. The obtained materials exhibit a mesoporous volume higher than the parent ferrierite with no significant effect on the sample acidity. The catalytic activity of some samples was investigated in vapour-phase methanol dehydration to dimethyl ether, revealing the superiority of hierarchical zeolites in terms of methanol conversion, although the presence of mesopores causes formation of light hydrocarbons at high temperatures.</jats:p>