Orientation dependence of the martensite transformation in a quenched and partitioned steel subjected to uniaxial tension
Contributor:
De Knijf, D.;
Nguyen-Minh, T.;
Petrov, R. H.;
Kestens, L. A. I.;
Jonas, John J.
Published:
International Union of Crystallography (IUCr), 2014
Published in:
Journal of Applied Crystallography, 47 (2014) 4, Seite 1261-1266
Language:
Not determined
DOI:
10.1107/s1600576714011959
ISSN:
1600-5767
Origination:
Footnote:
Description:
The orientation dependence of the austenite-to-martensite transformation during uniaxial tensile testing was modelled using the phenomenological theory of martensite crystallography and the mechanical driving force. It was validated experimentally by means of electron backscatter diffraction measurements on a pre-defined zone of a quenched and partitioned steel during interrupted tensile tests. A close match is obtained between the predictions of the model and the experimental observations.