Development of Ni catalysts with low metal content and improved stability in the dry reforming of methane to syngas
Hochschulschrift:
Dissertation, Universität Rostock, 2019
Anmerkungen:
GutacherInnen: Udo Kragl (Universität Rostock, Institut für Chemie, Abteilung Technische und Analytische Chemie) ; Martin Muhler (Ruhr-Universität Bochum, Lehrstuhl für Technische Chemie)
Beschreibung:
Catalysts with 2.5 wt% Ni supported on MgO-Al2O3 were developed for CH4 dry reform-ing (DRM) that are stable at either mild (stoichiometric) or severe (CH4-rich) conditions. Solid materials were characterized with suitable methods. Catalysts with NiO-MgO-Al2O3 solid solution were active even at 500 °C. In stoichiometric DRM, Ni catalyst modified with La and citric acid reduced both Ni re-oxidation and agglomeration, preserving high activity over 160 h. Besides, proper support pre-treatment or adding Gd3+ both offered outstandingly coking-resistant Ni-based catalysts for CH4-rich DRM over 100 h.<eng>
Für das trockene Reformieren (DRM) wurden Katalysatoren mit niedrigem Ni-Gehalt (2,5 Gew.-%) auf Mg-Al-Mischoxid entwickelt, die stabil bei stöchiometrischen oder CH4-reichen Bedingungen waren. Die Materialien wurden charakterisiert. Katalysatoren mit festen NiO-MgO-Al2O3-Lösungen waren schon bei 500 °C aktiv. Im stöchiometrischen DRM verringerte die Modifikation mit La/Zitronensäure die Reoxidation/Agglomeration von Ni und die Katalysatorstandzeit erreichte 160 h. Geeignete Trägervorbehandlung oder Gd3+-Dotierung führte zu stabilen und aktiven Ni-Katalysatoren für das CH4-reiche DRM über 100 h.<ger>