Cellulose hydrogels physically crosslinked by glycine: Synthesis, characterization, thermal and mechanical properties
Sie können Bookmarks mittels Listen verwalten, loggen Sie sich dafür bitte in Ihr SLUB Benutzerkonto ein.
Medientyp:
E-Artikel
Titel:
Cellulose hydrogels physically crosslinked by glycine: Synthesis, characterization, thermal and mechanical properties
Beteiligte:
Palantöken, Sinam
[Verfasser:in];
Bethke, K.
[Verfasser:in];
Zivanovic, V.
[Verfasser:in];
Kneipp, Janina
[Verfasser:in];
Rademann, Klaus
[Verfasser:in];
Kalinka, Gerhard
[Verfasser:in]
Erschienen:
BAM-Publica - Publikationsserver der Bundesanstalt für Materialforschung und -prüfung (BAM), 2019
Sprache:
Englisch
DOI:
https://doi.org/10.1002/APP.48380
Entstehung:
Anmerkungen:
Diese Datenquelle enthält auch Bestandsnachweise, die nicht zu einem Volltext führen.
Beschreibung:
Biopolymers are very efficient for significant applications ranging from tissue engineering, biological devices to water purification. There is a tremendous potential value of cellulose because of ist being the most abundant biopolymer on earth, swellability, and functional groups to be modified. A novel, highly efficient route for the fabrication of mechanically stable and natural hydrogels is described in which cellulose and glycine are dissolved in an alkaline solution of NaOH and neutralized in an acidic solution. The dissolving temperature and the glycine amount are essential parameters for the self-assembly of cellulose chains and for Tuning the morphology and the aggregate structures of the resulting hydrogels. Glycine plays the role of a physical crosslinker based on the Information obtained from FTIR and Raman spectra. Among the prepared set of hydrogels, CL5Gly30 hydrogels have the highest capacity to absorb water. The prepared CL5Gly30 gels can absorb up to seven times their dry weight due to its porous 3-D network structure. CL5Gly10 hydrogel exhibits 80% deformation under 21 N force executed. The method developed in this article can contribute to the application of heavy metal adsorption in aqueous solutions for water purification and waste management.