Beschreibung:
AbstractPolycondensation of the diacid chloride of 2‐(3‐carboxy vinyl)phenyl‐1,3‐dioxoisoindoline‐5‐carboxylic acid with m‐phenylenediamine and the diacid chloride of 2‐(4‐carboxy phenyl)‐1,3‐dioxoisoindoline‐5‐carboxylic acid with 1,5‐bis(3‐aminophenyl)1,4‐pentadien‐3‐one was carried out in polar solvents to produce new unsaturated polyamide–imides. The solution and the thermal, electrical, and a few other properties of the polymers were studies. The polymers were soluble in highly polar solvents. The solubility parameter of the polymers was calculated from the Small's group contribution. The polymers were fairly thermostable and underwent crosslinking creaction when heated, preferably in the presence of a suitable catalyst. The crosslinked polymers were in soluble even in highly polar solvents and possessed higher thermal stability. The swelling behavior of the polymers was studied and the molecular weight between two consecutive crosslinks was determined. X‐ray diffraction and the dielectric properties of the polymers and their crosslinked products were also studied.