Can the Cure Time of Endodontic Sealers Affect Bond Strength to Root Dentin?
Sie können Bookmarks mittels Listen verwalten, loggen Sie sich dafür bitte in Ihr SLUB Benutzerkonto ein.
Medientyp:
E-Artikel
Titel:
Can the Cure Time of Endodontic Sealers Affect Bond Strength to Root Dentin?
Beteiligte:
Mesquita, Gabriela Campos;
Verissimo, Crisnicaw;
Raposo, Luis Henrique Araujo;
Santos-Filho, Paulo Cesar Freitas;
Mota, Aderito Soares da;
Soares, Carlos Jose
Erschienen:
FapUNIFESP (SciELO), 2013
Erschienen in:
Brazilian Dental Journal, 24 (2013) 4, Seite 340-343
Beschreibung:
The cure time of endodontic sealers may influence the bond strength of fiber posts to root dentin. Forty teeth were selected and endodontically filled using calcium hydroxide cement and then divided into 2 groups according to the time elapsed between endodontic filling and post luting (n = 20): Immediately - glass fiber post luting immediately after endodontic filling; and Delayed - post luting performed 7 days after endodontic filling. The roots were also subdivided according to resin cement used for post luting (RelyX ARC and RelyX Unicem). The specimens were stored at 37°C for 24 h and sectioned in six 1-mm-thick slices from cervical, middle and apical thirds. The slice specimens were submitted to a push-out test at a crosshead speed of 0.5 mm/min, and the bond strength values obtained (MPa) were submitted to two-way ANOVA in a split-plot arrangement and Tukey's test (α=0.05). For both RelyX ARC and Unicem, the bond strength was significantly higher when the posts were cemented 7 days after the endodontic treatment. RelyX Unicem showed significantly higher bond strength values than RelyX ARC for both cementation periods. It was concluded that post luting should be made after the complete setting of the root canal sealer. Self-adhesive resin cement should be preferred for fiber post luting.