Sie können Bookmarks mittels Listen verwalten, loggen Sie sich dafür bitte in Ihr SLUB Benutzerkonto ein.
Medientyp:
E-Artikel
Titel:
Indentation Creep and Microstructure Properties of Sn-Ag Solder Alloys
Beteiligte:
Yassin, Amal Mohamed;
Khalifa, B.A.;
Ismail, R. Afify
Erschienen:
CIRWOLRD, 2019
Erschienen in:
JOURNAL OF ADVANCES IN PHYSICS, 16 (2019) 1, Seite 171-184
Sprache:
Nicht zu entscheiden
DOI:
10.24297/jap.v16i1.8243
ISSN:
2347-3487
Entstehung:
Anmerkungen:
Beschreibung:
<jats:p>The microstructure and micro-hardness of Sn-3.5wt.5%Ag, Sn-3.5wt.%Ag-0.27wt.%Ti and Sn-3.5wt.%Ag-0.27wt.%Cd treated at 75, 100, 125 and 150oC were studied. The microstructure characteristics of the tested alloys had been investigated using optical microscope (OM), scanning electron microscope (SEM) and x-ray diffraction (XRD). The impression creep had been carried out using Vickers micro-hardness indenter under different loads (10, 50 and 100gm). The stress exponent values were found to be varied from 3.2 to 8.4. The energy activating the creep processes support dislocation climb as the rate controlling mechanism. The dislocation mobility was restricted due to the agglomerations of the Ag3Sn eutectic phase in the above three solders. Whereas; the presence of the twinning of ?-Sn phase, and the dispersion of fine CdSn1.9 IMCs throughout Sn-3.5wt.%Ag-0.27wt.%Cd made strongly blockage of the dislocation motion.</jats:p>