<jats:p>Ti<jats:sub>60</jats:sub>(Ni<jats:sub>x</jats:sub>Cu<jats:sub>40-x</jats:sub>)<jats:sub>40</jats:sub> x = 5 - 40 at% ternary alloys were prepared by arc-melting followed by a centrifugal casting into a wedge-shaped copper mould in order to examine glass forming of these compositions. Microstructure of the master alloys and wedge-shaped samples were studied. Among the master alloys, which solidified under non-equilibrium conditions, the sample with 15 at% Ni content displayed clear eutectic structure and its wedge-shaped sample had the finest structure but still crystalline. Microstructure of the other compositions was far from amorphous state.</jats:p>