Beschreibung:
The partitioning of ferric iron between chromian spinel and basic silicate melt was studied experimentally. Runs were carried out at temperatures of 1 180-1 300 °C and oxygen fugacities of 10-3-10-9 atm, at one atmosphere total pressure. A linear relationship exists between the Fe2O3 content of chromian spinel (known by microprobe analysis) and the Fe2O3 content of the liquid (calculated from the empirical relation established by Kilinc et al., 1983). The partition coefficient, DT = (Fe2O3)sp/(Fe2O3)liq, depends on temperature, but neither on fO2 nor on the Fe total content of the melt : log DT = 4 8 13/T — 2.39. The Fe2O3 content of spinel is related to physico-chemical parameters as follows : [formula] It is pointed out that, at constant temperature and oxygen fugacity, (Fe2O3)sp is a linear function of the total iron content of the melt.
On détermine expérimentalement la distribution du fer ferrique entre spinelle chromifère et bain silicaté basique en équilibre, sous une pression totale de 1 atm, entre 1 180 et 1 300 °C, et pour des fugacités d'oxygène comprises entre 10-3-10 et 9 atm. Une relation linéaire entre les teneurs en Fe2O3 des spinelles (déduites de l'analyse à la microsonde) et celles des liquides (calculées par la formule de Kilinc et al., 1983) est mise en évidence : (Fe2O3)sp = DT (Fe2O3)liq. Le coefficient de distribution DT est fonction de la température : log DT = 4 8 13/T — 2,39. Il est indépendant de fO2 et de la teneur en fer du bain. La teneur en Fe2O3 du spinelle est reliée aux paramètres physico-chimiques par la formule : [formula] qui permet de chiffrer le rôle de chacun de ces facteurs. Un fait remarquable est la proportionnalité entre (Fe2O3)sp et la quantité de fer totale du bain, à température et fugacité d'oxygène constantes.